Henan Hongtai Kiln Refractory Co.,Ltd.
PROFESSIONAL MANUFACTURE REFRACTORIES FOR FURNACE ！
|
Verified Supplier
2 Years |
Place of Origin : Henan, China
Shape : Brick
Material : Magnesia Lron Spinel Brick
SiO2 Content (%) : Customized
Al2O3 Content (%) : 3~7
MgO Content (%) : Customized
CaO Content (%) : Customized
Refractoriness (Degree) : 1770°< Refractoriness< 2000°
CrO Content (%) : Customized
SiC Content (%) : Customized
Model Number : HT
Brand Name : Hongtai
Processing Service : Bending, Welding, Punching, Decoiling, Cutting, Moulding
Product Name : Refractory Brick
Raw Material : Magnesia Lron
Advantage : Thermal Shock Resistance
Certificate : ISO9001 CE
Application : High Temperature Tunnel Kiln
Brand : Rongsheng
MgO % : 88
Fe2O3 % : 4~5
Al2O3 % : 3~5
Bulk density g/cm3 : 2.95
MOQ : 500 tons
Price : $0.92 - $8.20/tons
Description of Chemically erosion resistant Magnesia Iron Spinel
Magnesia-iron spinel bricks are made of bivalent iron aluminum spinel (FeO Al2O3) and high-purity magnesia as the main raw materials. During the firing process, the firing temperature and firing atmosphere are strictly controlled to ensure that the iron in the brick is oxidized. The substance exists in the form of FeO.
During the use of mafic-iron spinel bricks, a layer of highly viscous calcium-iron and calcium-iron-aluminum compounds is formed on the hot surface of the brick, which is easy to hang on the kiln. In addition to the excellent kiln-hanging properties of magnesia-chrome bricks, magnesia-iron spinel bricks also have higher thermomechanical and thermochemical properties.
Sprcifications of Chemically erosion resistant Magnesia Iron Spinel
| Iterm | Indicators | |
| MgO% | ≥ | 85 |
| Fe2O3% | 5-7.5 | |
| Al2O3% | 3-5 | |
| SiO2% | ≤ | 2 |
| Bulk Density (g/cm3) | ≥ | 3 |
| Apparent Porosity % | ≤ | 17 |
| Cold Crushing Strength (Mpa) | ≥ | 45 |
| Refractoriness under Load T0.6 (℃) | ≥ | 1600 |
| Thermal shock resistance(1100℃ water quenching,cycle) | ≥ | 6 |
| Thermal conductivity coefficienW/m.k | ≤ | 2.6 |
Packing of Chemically erosion resistant Magnesia Iron Spinel
1.on wooden pallets with plastic cover: wooden pallet size :930*930 or 1000*1000mm,
2.Load weight of each pallet: 1.5-2.0 tons,
3.230*114*65mm:512PCS/Pallet, 230*114*75mm:448PCS/Pallet.
Shipping of Chemically erosion resistant Magnesia Iron Spinel
1.Our packaging is as per customer’s request
2.Normal goods delivered by sea transport
3.Sample shipping by express
4.We will shipping and delivery goods timely, quanlity and quantity guaranteed, and also in accordance with the contract and customer's requirment completely.
|
Advanced Magnesia Iron Spinel Brick for Cement Rotary Kiln Firing and Transition Zone Images |
Low Apparent Magnesia Carbon Refractory Bricks For Ladle Lip With And Low SiC
High Magnesia Gunning Mix Refractory International Standard and Good Volume
Al2O3 Content Below 25% Fused Clinker Magnesium Chrome Brick for Cement Rotary
18% Apparent Porosity Electric Fused Magnesia Chrome Refractory Brick for Power
Superior Performance Magnesia Chrome Refractory for Cement Rotary Kiln Furnace
12% CrO Content Magnesia Chrome Refractory Fire Bricks for High Temperature
Steel Ladle Magnesium Carbon Refractory Bricks with Cold Crushing Strength MPa
Tundish Bricks Magnesia Brick with Customizable Specifications and 92% MgO
Common Refractoriness 1580° Refractoriness 1770° Magnesite Chrome Brick for
Low Apparent Porosity Magnesia Carbon Brick For Converter Mouth With Excellent